Quality & R&D

화학성분
기계적 성질
좌, 우 드래그가능
재질
(규격)		 질별 인장강도
(N/mm2)		 항복강도
(N/mm2)		 연신율
(%)		 시험위치의 두께
(mm)		 비고
(규격)		 HRF HWEB HV
A6063 T5 150 110 8 12 ↓ KS D 6759 65 10 62
T6 205 170 8 3 ↓ 78 13 80
A6061 T4 175 110 16 - KS D 6759 70 12 68
T6 265 245 8 6 ↓ 80 14 89
A6082 T5 290 250 8 15 ↓ KS D 6759 78 13 80
T6 310 260 8 15 ↓ 85 15 92
A6005 T5 250 200 8 6 ↓ KS D 6759 80 13 82
T6 260 215 8 6 ↓ 82 14 84
DIN EN 755-2

Alloy EN AW-6005[Al SiMg]and Alloy EN AW-6005A[Al SiMg(A)]

Temper Wall thickness
t
mm
Rm
MPa
Rp0.2
MPa
A
%
min.
A50 mm
%
min.		 Hardness
Typical
value
HBW
min. max. min. max.
T6 c ≤ 5 270 - 225 - 8 6 90
5 < t ≤ 10 270 - 225 - 8 6 90
T4 c ≤ 25 320 - 220 - 16 14 85
T6 c ≤ 25 380 - 360 - 10 8 120
O,H111 ≤ 25 - 150 - 110 16 14 30
T4 c ≤ 25 180 - 110 - 15 13 65
T6 c ≤ 25 240 - 240 - 8 6 95
260 - 240 - 10 8 95
O,H111 ≤ 25 - 130 - - 18 16 25
T4 c ≤ 10 130 - 65 - 14 12 50
10 < t ≤ 25 120 - 65 - 12 10 50
T5 ≤ 25 175 - 130 - 8 6 65
T6 c ≤ 25 215 - 170 - 10 8 75
T66 c ≤ 25 245 - 200 - 10 8 80
O,H111 ≤ 25 - 160 - 110 14 12 35
T4 c ≤ 25 205 - 110 - 14 12 70
T6 c ≤ 25 290 - 250 - 8 6 95
≤ 5 < t ≤ 25 310 - 260 - 10 8 95